A-A-665E
Government. The Government reserves the right to perform any of the inspections set forth herein when deemed necessary to assure that the paint conforms to the prescribed requirements. Failure to meet any requirement shall be cause for rejection of the lot from which the sample was taken.
3.3 Table of characteristics.
|
Characteristics |
Limits |
ASTM Method |
|
Total solids, grams |
|
|
|
D 2369 |
|
|
|
Clear |
22 min. |
|
|
Flat Black |
40 min. |
|
|
Gloss Black |
45 min. |
|
|
Brass |
38 min. |
|
|
Silver |
25 min. |
|
|
Other colors |
54 min. |
|
|
Specular Gloss |
|
D 523 |
|
Gloss colors |
75 min. |
|
|
Semi-gloss |
20-50 min. |
|
|
Flat |
15 mi. max. |
|
|
Constant Ratio |
|
D 2805 |
|
(at 1.0 +/- 0.2 mil dry film thickness sprayed on Leneta or Morest hiding power charts) |
|
|
|
Black, Silver and Gold |
0.98 min. |
|
|
Red, Yellow and Orange |
0.80 min. |
|
|
White |
0.85 min. |
|
|
Other colors |
0.94 min. |
|
|
Drying time |
|
Fed-Std-141C |
|
Set to touch, min. |
15 max. |
4061.2 |
|
Dry through, Hr. |
2.0 max. |
|
|
Afterback free, Hr. |
48 max. |
|
|
Lead content, % by weight of non-volatile |
0.06 max. |
D 3335 |
|
Hexavalent Chromium Content2 |
None to limits of defection |
|
3.3.1 Flexibility.1 The paint film shall bend over a 1/4 inch cylindrical mandrel without cracking or flaking (Fed-Std- 141C, method 6221).
3.3.2 Self-Lifting.1 When recoated after drying for 2, 24 and 48 hours, the paint shall not wrinkle or lift.
3.3.3 Water resistance.1The film shall not wrinkle or blister after 18 hours immersion in distilled water at 73o +/- 2oC (ASTM D 1308). The color change, delta E, one hour after removal shall not be greater than 2.5 (ASTM D 2244).
3.3.4 Technical Footnotes: