MIL-DTL-24441/35B(SH)
QUANTITATIVE REQUIREMENTS: The paint shall meet the following quantitative requirements and the
qualitative requirements of section 3 of the general specification. The components A and B shall be mixed 1:1 by
volume for mixed component tests. Tests shall be performed in accordance with the general specification.
Component A
Component B
Mixed components
Requirements
Min
Max
Min
Max
Min
Max
Pigment content, percent (%)
48.0
54.0
28.0
33.0
---
---
Volatiles, %
24.0
29.0
17.0
22.0
---
---
Nonvolatile vehicle, %
17.5
23.5
48.0
53.0
---
---
Water, %
---
1.5
---
0.5
---
---
Coarse particles, %
---
0.3
---
0.3
---
---
Consistency, grams
---
310
---
410
---
---
Kilograms per liter (kg/L)
1.43 (11.9)
1.58 (13.2)
1.26 (10.5)
1.38 (11.5)
---
---
(pounds per gallon (lb/gal))
Set to touch, hours
a. at 4.4 C (40 F)
---
---
---
---
---
3
b. at 23 C (73 F)
---
---
---
---
---
3
Dry-hard, hours
a. at 4.4 C (40 F)
---
---
---
---
---
24
b. at 23 C (73 F)
---
---
---
---
---
8
Fineness of grind, NS
4
---
4
---
---
---
Flash point, C (F)
35.6 (96)
---
37.8 (100)
---
35.6 (96)
---
Titanium dioxide, % of pigment
13
---
---
---
---
---
Pot life, hours at 23 C (73 F)
---
---
---
---
4
---
Sag resistance, micrometers
---
---
---
---
300 (12)
---
(mils)
Color of dry film to approximate
---
---
---
---
Conform
the standard color chip
Weight per epoxy vehicle
---
---
175
195
---
---
Contrast ratio, 3-mil dry film
---
---
---
---
0.98
---
thickness
Gloss, 60 degree specular, %
---
---
---
---
---
25
VOC, grams per liter (g/L)
---
---
---
---
---
340 (2.8)
(lb/gal)
See footnotes on next page.
2