MIL-PRF-14105E
TABLE II. Index.
Requirement
Item
ASTM Method
Test Paragraph
Paragraph or Table
Color
-
4.8
3.2
Pigment analysis
D2371
4.9
3.4.1 and Table I
Hexavalent chromium
-
4.10
Table I
Cadmium content
D3335
-
Table I
Lead content
D3335
4.11
3.4.2 and Table I
VOC content
D3960
4.12.1
3.4.3 and Table I
VOHAP content
D3271
4.12.2
3.4.4 and Table I
Condition in container
-
4.13
3.6.1
Accelerated storage
-
4.14.1
3.6.2.1
stability
Full container storage
D1849
4.14.2
3.6.2.2
stability
Brushing properties
-
4.15
3.6.3
Spraying properties
-
4.15
3.6.3
Dry opacity, contrast ratio
D2805
4.16
Table I
Viscosity, Krebs-Stormer
D562
4.17
Table I
Fineness of grind
D1210
-
Table I
Suspension properties
-
4.18
3.6.4
Specular gloss (60 degree)
D523
4.19
Table I
Drying properties:
Air drying
D5895
4.20.1
3.6.5.1
Baking
D5895
4.20.2
3.6.5.2
Water resistance
D870
4.21
3.6.6
JP8 resistance
-
4.22
3.6.7
Salt spray resistance
B117
4.23
3.6.8
Accelerated weathering
G155
4.24
3.6.9
Recoating
-
4.25
3.6.10
Adhesion by tape test
D3359
4.26
3.6.11
High temperature
resistance:
Heat exposure cycle
-
4.27.1
3.6.12.1
Salt spray
B117
4.27.2
3.6.12.2
Quenching cycle
-
4.27.3
3.6.12.3
Accelerated weathering
G155
4.27.4
3.6.12.4
Toxic ingredients
-
4.28
3.6.13
HAP ingredients
-
4.29
3.6.17
4.7 Surface preparation of test panels.
4.7.1 Test panels. Unless otherwise specified herein, test panels shall be rust free cold rolled steel
panels 0.1875 inches (4.7625 mm) gauge by 3 inches (76.2 mm) width by 6 inches (152.4 mm)
length. The panels shall be solvent cleaned in accordance with SSPC-SP 1 solvent cleaning, after