TT-P-28H
TABLE I. Quantitative requirements.
Requirements |
Requirements |
|
Minimum |
Maximum |
|
Total solids, percent by weight of paint |
40 |
--- |
Pigment, percent by weight of paint |
23 |
27 |
Vehicle solids, percent by weight of paint |
18 |
--- |
Silica (Si02), percent by weight of vehicle solids |
30 |
--- |
Water content, percent by weight of paint |
--- |
0.2 |
Consistency (package), kreb stormer shearing rate 200 RPM (grams) |
100 |
150 |
Equivalent kreb units (KU) |
61 |
72 |
Flash point, °C (°F) |
38(100) |
--- |
Drying time, hours (Type I) |
||
Set to touch (ambient dry) |
--- |
1 |
Dry hard (ambient dry) |
--- |
3 |
Full hardness, heat cure baked at 204 °C (400 °F), hours |
--- |
1 |
Full hardness (Type II), baked at 204 °C (400 °F), minutes |
--- |
20 |
V0C, grams per liter [g/L] (pounds per gallon [lb/gal]) Type I/Type II |
--- |
250/75 (2.08/0.62) |
Asbestos, percent by weight in dry film |
--- |
0.1 |
3.3.1 Color. When tested in accordance with Table IV, the color of the final paint dry film shall match color 17178 of FED-STD-595.
3.3.2 Solvents and hazardous air pollutant (HAP) content. When tested in accordance with 4.5.17, the solvents and HAPs content in the paint shall not exceed the percent by weight (%WT) values listed in Table II. Within these limitations and the requirement that the finished paint meet all requirements of this specification, solvent selection is the responsibility of the manufacturer.