MIL-PRF-25134C(USAF)
3.6 Viscosity. When tested at 77° 3°F as specified in 4.7.3 the remover shall have a viscosity
of not less than 6.0 or more than 14.0 poises.
3.7 Volatility. The volatility of the paint remover shall be equal to or less than the volatility of
distilled water, when tested as specified in 4.7.4.
3.8 Removal power. When tested as specified in 4.7.5, the remover shall loosen, soften, and
remove enamel and lacquer finishes as well as, or better than, the paint stripping efficiency
comparison formula product (see 4.5).
3.9 Rinsability. When tested as specified in 4.7.6, enamel and lacquer films that have been lifted
by the remover shall be as completely and readily removed by flushing with a stream of water as
those lifted by the comparison formula.
3.10 Coating residue. The remover shall leave no coating residue or remover residue greater
than that left by the comparison formula on stripped and water-rinsed metal surfaces when tested
as specified in 4.7.7.
3.11 Remover residue. The remover shall leave no more residue than the comparison formula on
bare or pretreated metal surfaces when tested as specified in 4.7.8.
3.12 Corrosion. The remover shall not corrode uncoated steel, cadmium plated steel, tinplate,
aluminum alloy, magnesium, or combinations thereof when tested as described in 4.7.9.
3.13 Hydrogen embrittlement. When tested as specified in 4.7.10, there shall be no evidence of
hydrogen embrittlement of the test specimen. Failure of any specimen of the test group
constitutes failure of the entire group.
3.14 Flammability. The remover shall not continue to burn after removal of an externally applied
flame when tested as specified in 4.7.11.
3.15 Cold stability. When tested as specified in 4.7.12, remover that has been cooled to 14°
2°F for 4 hours, then returned to room temperature shall be as readily dispersed to its original
appearance and consistency as an uncooled sample. After standing for 1 hour without agitation,
the cooled sample shall show no more settling than an uncooled sample.
3.16 Storage stability. After 6 months storage as specified in 4.7.13, the remover shall conform
to all of the requirements of this specification.
3.17 Service test. The remover, when tested as specified in 4.7.14 shall show satisfactory
performance in actual use.