gal\) maximum] volatile organic content \(VOC\) complying paint. The paint is a special-purpose white alkyd enamel \(Formula Number 30\) for interior use, either primed steel or primed aluminum \(see 6.1\). This product may be used wherever VOC air pollution regulations apply. Product is supplied in a single can and used as supplied without thinning.

Pages 1 - 2 - 3 - 4 - 5 - 6 - 7 - 8 - 9 - 10 - 11 - 12 - 13

MIL-DTL-1115E

TABLE VII. Test procedures � Continued.

FED-STD-141

ASTM test

Test

Requirement

Test

test method

method

Drying time

----

D5985

Dry to touch 1/

Table III

Table VII

Dry through

Fineness of grind 1/

Table III

Table VII

----

D1210

Flash point 1/

Table III

Table VII

----

D3278

Gloss 1/

Table III

Table VII

----

D523

Sag resistance 1/

Table III

Table VII

----

D4400

Odor

3.4.1

Table VII

----

D1296

3.4.2

4.5.12

----

E1347/D2244

Color and

Surface appearance 1/

3.4.10

4.5.13

3011.1

----

Flexibility

3.4.3

4.5.7

6221

----

Condition in container

3.4.5

4.5.8

3011.2

D869

Storage stability

Full container

3.4.5.1.1

4.5.9.1

3011.1

D869/D1849

Partially full container

3.4.5.1.2

4.5.9.2

3021.1

F718

Brushing properties

3.4.6.1

Table VII

4321.2

----

Spraying properties

3.4.6.2

Table VII

2131.1/4331.1

----

Rolling properties

3.4.6.3

Table VII

4335

----

Compatibility with

----

Topcoats

3.4.9.1

4.5.11.1

4.5.9.1

Primer and undercoats

Contrast ratio 1/

----

D2805

3.4.10.1 and

----

D3363

Pencil hardness

Off-gassing

----

NOTES:

Conformance inspection test (see 4.3).

By data certification.

4.5 Test methods and test panel preparation. Test methods shall be in accordance with table VII.

4.5.1 Panel preparation. Steel panels [minimum size 60 mm by 90 mm by 3 mm (2.4 inches by 3.6 inches by

0.12 inch) thick (nominal)] shall be prepared for testing by abrasive blasting to a near white metal surface in

accordance with SSPC-SP 10 to achieve a minimum 0.051 mm (0.002 inch; 2.0 mil) surface profile. The blasted

panels shall be solvent wiped to remove any traces of oil or residue, blown dry with dry air, wrapped in plastic and

stored in a desiccator, oven, air-tight storage bag or use other means to prevent rusting prior to coating. The

abrasive used for blasting shall be in accordance with MIL-A-22262 and be listed on the current qualified products

list. Unless otherwise specified in the applicable test paragraphs of this specification, the test panels shall be coated

with TT-P-645 primer applied in one coat at a wet film thickness that will yield a dry film thickness 50 percent

greater than the blast profile. Unless otherwise specified, dry time shall be 48 hours at 21 �C (70 �F). Unless

otherwise specified in this specification, film thickness for test purposes shall be achieved by use of a 0.006 draw

down blade which yields a 0.003-inch wet film thickness.